UV Adhesive for Glass Furniture
from Tina(hengying@cnhybond.com 0086-18927302778 Skype:hengying11)
Description
Fast curing, high strength Ultra Violet adhesive, specially designed for bonding glass to glass, glass to crystal, glass to metal, even Glass to Aluminum cake and glass to Stainless Steel bonding in the manufacturing of glass and crystal table. It’s suitable for safety glass and color glass (partly UV radiation absorbing).
Physical properties
Composition: methacrylate ester
Color: colorless
Viscosity (Brookfield 25°C–mPa.s): 600 - 1300
Specific weight (g/ml): 1.1 and 1.4
Curing time UV (365 nm): 8 – 15 seconds
Gap to fill: from 0.03 mm to 1.5 mm
Flash point: > 100°C
Shelf life: 1 year
Main Performance(Glass/Metal)：
Items
|
Performance
|
Type
|
HYBOND 303(1) UV Adhesive
|
303（2）UV adhesive
|
Color
|
Clear or yellowish
|
Clear
|
Viscosity 25℃
|
650-700 MPa.s
|
3000±500
|
Solidify time
|
About 10s
|
About 10s
|
Refraction
|
1.47-1.50
|
1.47-1.50
|
Storage
|
Room temperature, avoid sunlights
|
Curing properties
For better strength and durability we recommend to clean, degrease and dry surfaces to bond. The polymerisation UV belongs to the intensity of the UV lamp, to the distance from the UV light source, to the bondline gap and to the light transmittance of the substrate the light shall pass through. We recommend high inensity UV light sources with minimum radiation between 365 nm and 420 nm at 100mW/cm2., curing time may vary according to adhesive gap.
Properties of cured adhesive
* Tensile strength (ASTM D-2095-69): 10 - 14 N/mm²
* Temperature range: -55°C + 120°C
* Refractive index: 1.49
* Light transmittance: > 98%
* Coefficient of thermal expansion: 85 x 10-6 mm/mm/°C
* Dieletric constant (25°C 1000 Hz): 4
* Dieletric strength 10-12 KV/mm
Storage
Keep product in a cool and dry room at +28°C. To avoid contaminations do not refill containers with used product. For more information on applications, storage and handling contact HYBOND Technical Service
Note
The data contained herein, obtained in HYBOND laboratories, are given for information only. HYBOND cannot assume responsibility for the results obtained by others which methods are not under HYBOND control. It is the user's responsibility to determine suitability for the user's purpose of any product mentioned herein. HYBOND disclaims all warranties expressed or implied, including warranties of merchantability or fitness for a particular purpose, arising from sale or use of HYBOND products. HYBOND specifically disclaims any liability for consequential or incidental damages of any kind, including lost profits.
n:'yes� � o t �Ȟ �� Trebuchet MS'; mso-fareast-font-family:宋体; color:rgb(0,0,0); font-size:10.5000pt; mso-font-kerning:0.0000pt; " >N·m 16.9 to 34LMS (lb.in.) (150 to 300)
3/8 x 16 zinc nuts and bolts N·m 16.9 to 34LMS (lb.in.) (150 to 300)
M10 steel nuts and bolts N·m 23 to 40 (lb.in.) (200 to 350)
4. Assembly
(1). For best results, clean all surfaces (external and internal) with a HYBOND cleaning solvent and keep it dry.
(2). If the cure speed is too slow, use appropriate activator. Please see the Cure Speed vs. Activator graph for reference. Allow the activator to dry when needed.
(3). Shake the product thoroughly before use.
(4). To prevent the product from clogging in the nozzle, do not allow the tip to touch metal surfaces during the process of application.
(5). For Thru Holes, apply several drops of the product onto the bolt at the nut engagement area.
(6). For Blind Holes, apply several drops of the product down the internal threads to the bottom of the hole
(7). Sealing Applications,
Applying a 360° bead of product to the leading threads of the male fitting, keep the first thread free, force the material into the threads to thouroughly fill the voids. For bigger threads and voids, adjust product amount accordingly and apply a 360° bead of product on the female threads also.
(8). Assemble and tighten as required.
5. Disassembly
Apply localized heat to nut or bolt to approximately 250°C. Disassemble while hot.
6. Cleaning up
Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.
7. Storage
Store product in the unopened container in a dry location, storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.
8. Note
The data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtained by others over whose methods we have no control. It is the user's responsibility to determine suitability for the user's purpose of any production methods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of persons. From any hazards that may be involved in the handling and use thereof. In light of the foregoing, HENG YING Corporation specifically disclaims all warranties expressed or implied, including warranties of merchantability or fitness for a particular purpose, arising from sale or use of HENG YING Corporation’s products. HENG YING Corporation specifically disclaims any liability for consequential or incidental damages of any kind, including lost profits.